PP-HFAST

Hybrid hi-performance polyaspartic (fast)

PP-HFAST is a two-component, 85% solid, rapid curing, hybrid polyaspartic coating system designed as a decorative yet durable coating for commercial and industrial flooring. Formulated with aliphatic chemistry, PP-HFAST is color stable allowing it to take UV exposure without color shifts seen with other coating systems such as epoxies. PP-HFAST is a 1:1 mix ratio system with sufficient pot life to be rolled, brushed, or sprayed . It has a robust application window with ability to apply at low temperatures and high humidity.

Advantages

  • Lower odor than most polyaspartics
  • Cures at temperatures just above freezing
  • Can be applied below -20°F (-28.9°C). Will cure with special handling
  • Excellent UV resistance, non yellowing and high gloss characteristics
  • Excellent color stability
  • Achieve a variety of colors, patterns, and logos, using decorative flakes, particles, or signs
  • Excellent abrasion and impact resistance
  • Available in low VOC and also in zero VOC formulation for restricted areas such as Southern California
  • Micro media traction agents can be introduced into the liquid system or dispersed into the top coat
  • Excellent chemical resistance, resistant to skydrol
  • Resistant to hot tire peel
  • Excellent coefficient of friction properties
  • High build capability in lifts of 10 – 12 mils maximum
  • Can be matted with a matting agent
  • Bonds to virtually all substrates of any dimension,including metals, concrete, and fiberglass
  • Tolerant to 300°F (149°C) for random, incidental heat contact

Where to use

  • Marine protection for fiberglass, steel, concrete or wood
  • UV-stable top coat
  • Aircraft hangar floors
  • Low temperature equipment
  • Maintenance facilities
  • Offshore platforms
  • Industrial shop floors
  • Secondary Containment
  • Cooling towers
  • Bridges
  • Wastewater treatment applications

Technical Data

IMPORTANT NOTE: PROPERTIES @ 73°F (23 °C) and 50% R.H. Times are approximate and will be affected by changing ambient conditions, especially changes in temperature and relative humidity. The indicated mileage is calculated for flat surfaces. A porous or imperfect surface will require more material in order to cover the same mileage. *

PACKAGING2 US GAL KIT (7.57 L) or 10 US GAL KIT (37.8 L)
COLORUpon Request
RECOMMENDED THICKNESSPrimer - 8 MILS (200 ft²/gal)
Finish Coat:
- over solid color : 6 MILS (266 ft²/gal)
- over vinyl chips : 10 MILS (160 ft²/gal)
SHELF LIFE12 months in original unopened factory sealed containers. Keep away from extreme cold, heat, or moisture. Keep out of direct sunlight and away from fire hazards.
MIX RATIO, BY VOLUMEA:B = 1:1
MIX RATIO, BY WEIGHTA:B = 100:110
POT LIFE 16 OZ (454 G)15 minutes @ 77°F (25°C)
VOC0 g/L
SOLIDS CONTENT, BY VOLUME (CLEAR)PART A: 93%
PART B: 78%
MIX: 85%
SOLIDS CONTENT, BY WEIGHT (CLEAR)PART A: 92%
PART B: 75%
MIX: 83%
DENSITY (KG/L)PART A: 1.06
PART B: 1.15
MIX: 1.11
THINNER RECOMMENDEDXylene
DRYING TIMESTack-Free : 1 - 2 hours
Recoat Time: 2 hours
Foot Traffic: 2 - 4 hours
Heavy Equipment Traffic: 24 hours
Full Cure: 4 - 7 days
ABRASION RESISTANCE, ASTM D4060 TABER ABRASER CS-17 WHEEL / 1000G (2.2 LBS.) / 1000 CYCLES30 mg loss
ADHESION, ASTM D4541Concrete-primer : > 550 psi (substrate ruptures)
WATER ABSORPTION, ASTM D5700.2 %
WATER VAPOUR TRANSMISSION, ASTM E96Water procedure B Film 0.01cm (0.004″) : 1 perm
HARDNESS (SHORE D), ASTM D224075-78
FLEXIBILITY, 1/8” MANDREL, ASTM D1737Pass
FALLING SAND ABRASION RESISTANCE (L SAND/ 1 DRY MIL), ASTM D96845
VISCOSITY @ 77°C (25°C)Part A: 350-450 cps
Part B: 75-100 cps A/B
Mix: 125-225 cps
GLOSS, ASTM D52395+