PP-100SX

Hybrid 100% solid hi-performance polyaspartic

PP-100SX is a two component 100% solid, polyaspartic coating system. It provides outstanding appearance, superior chemical, U.V.,and solvent resistance. It exhibits excellent physical properties.

Advantages

  • No odor
  • Long working time (40 min to 1 hour)
  • UV resistant
  • Flexible
  • Very fast drying in thin film
  • Superior chemical resistance (very good stain resistance)
  • Superior weather and abrasion resistance
  • Non yellowing and good gloss retention
  • Dense surface resistant to bacteria and humidity
  • May be applied several layers on itself
  • Contains no VOC solvents, allowing for interior application without harmful odors
  • Excellent adhesive properties, allowing application on other firm and hard coating, as well as a good bond to the substrate

Where to use

  • UV-stable top coat
  • Aircraft hangar floors
  • Low temperature equipment
  • Maintenance facilities
  • Offshore platforms
  • Industrial shop floors
  • Car washes or wash bays
  • Primary and Secondary Containment
  • Cooling towers
  • Bridges
  • Wastewater treatment applications

Technical Data

IMPORTANT NOTE: PROPERTIES @ 73°F (23 °C) and 50% R.H. Times are approximate and will be affected by changing ambient conditions, especially changes in temperature and relative humidity. The indicated mileage is calculated for flat surfaces. A porous or imperfect surface will require more material in order to cover the same mileage. *

PACKAGING2.5 US GAL KIT (7.57 L) or 10 US GAL KIT (37.8 L)
COLORUpon Request
RECOMMENDED THICKNESSPrimer - 8 MILS (200 ft²/gal)
Finish Coat:
- over solid color : 6 MILS (266 ft²/gal)
- over vinyl chips : 10 MILS (160 ft²/gal)
SHELF LIFE12 months in original unopened factory sealed containers. Keep away from extreme cold, heat, or moisture. Keep out of direct sunlight and away from fire hazards.
MIX RATIO, BY VOLUMEA : B = 1.5 : 1
POT LIFE (454 G)15 minutes @ 77°F (25°C)
VOC0 g/L
SOLIDS CONTENT, BY VOLUME (CLEAR)PART A: 93%
PART B: 78%
MIX: 85%
SOLIDS CONTENT, BY WEIGHT (CLEAR)PART A: 92%
PART B: 75%
MIX: 83%
DENSITY (KG/L)PART A: 1.06
PART B: 1.15
MIX: 1.11
DRYING TIMESTack-Free : 1 - 2 hours
Recoat Time: 2 hours
Foot Traffic: 2 - 4 hours
Heavy Equipment Traffic: 24 hours
Full Cure: 4 - 7 days
ABRASION RESISTANCE, ASTM D4060 TABER ABRASER CS-17 WHEEL / 1000G (2.2 LBS.) / 1000 CYCLES4 mg loss
ADHESION, ASTM D4541Concrete-primer : > 550 psi (substrate ruptures)
WATER ABSORPTION, ASTM D5700.2 %
WATER VAPOUR TRANSMISSION, ASTM E96Water procedure B Film 0.01cm (0.004″) : 1 perm
HARDNESS (SHORE D), ASTM D224075-78
FLEXIBILITY, 1/8” MANDREL, ASTM D1737Pass
FALLING SAND ABRASION RESISTANCE (L SAND/ 1 DRY MIL), ASTM D96845
VISCOSITY @ 77°C (25°C)Part A: 350-450 cps
Part B: 75-100 cps A/B
Mix: 125-225 cps
GLOSS, ASTM D52395+

Documentation